Ibintu | Parameter | |
Ubuhanga Ibigize | SiO2+ Al2O3(wt%) | 48 ~ 58 |
CaO + MgO (wt%) | 36 ~ 46 | |
Fe2O3(wt%) | < 3 | |
Abandi (max; wt%) | ≤6 | |
Gutakaza Ignition (800 ± 10 ℃, 2H; wt%) | < 1 | |
Umubiri Ibyiza | Ibara | Kwera |
Igihe kirekire Ukoresheje Ubushyuhe | 600 ℃ | |
Impuzandengo ya fibre igereranijwe (μm) | 6 | |
Uburebure bwa fibre ifite uburemere buringaniye (μm) | 320 ± 100 | |
Kurasa ibirimo (> 125μm) | ≤2 | |
Ubucucike bwihariye (g / cm3) | 2.9 | |
Ibirungo (105 ± 1 ℃, 2H; wt%) | ≤2 | |
Ibikoresho byo kuvura hejuru (550 ± 10 ℃, 1H; wt%) | < 1 |
Ubuso bwubwoya bwa slag bworoshye kandi buringaniye, kandi igice cyacyo ni uruziga rwuzuye.Ibi biterwa ahanini nuko itanura ry itanura riturika rigabanuka kumiterere yumuzingi hamwe nubuso buto bwubutaka munsi yubushyuhe bwo hejuru mbere yo gukonja no gukomera muri fibre.
Iyo coefficente ya acide ari 1.0-1.3, fibre ya plaque itanura iturika iba yoroheje kandi fibre itunganijwe neza;hamwe no kwiyongera kwa coefficient ya acide, diameter ya fibre ikunda kwiyongera, kandi mugihe kimwe, umubare muto wimipira ya slag ushyirwa mumibabi, kandi ubwiza bwa fibre bukangirika.Muri rusange, hejuru ya coefficient ya acide, niko imiti iramba yubwoya bwa slag.Ariko, iyo coefficente ya acide iba ndende cyane, fibre yavuyemo irashobora kuba ndende.Nubwo imiti ihagaze neza, biragoye gushonga, fibre iba ndende, ndetse ntishobora no guhinduka fibre.Kubwibyo, mubikorwa nyabyo, coefficent ya acide yubwoya bwa slag irashobora kubikwa gusa kuri 1.2, kandi biragoye kugera kuri 1.3.
● Non asibesitosi
Amababi ya slag yubwoya bwa fibre nta asibesitosi afite kandi birashobora kuba ubundi buryo bwiza bwa asibesitosi mugukoresha friction.Niki cyingenzi, ni ku giciro cyo hasi cyane kuruta asibesitosi.
Loss Igihombo gito
Ku bushyuhe bwinshi, ibintu bimwe na bimwe bidakoreshwa muri fibre minerval bizatwikwa, bikaviramo gutakaza fibre ku gipimo cyo gutwika.Slag yubwoya bwa fibre fibre ni fibre organique idafite ibinyabuzima byose, kuburyo bigoye kugira igipimo cyo gutwika fibre.
Ibirimo amafoto make cyane
Ibirimo kurasa HB11X birashobora kugenzurwa munsi ya 2% nyuma yinshuro esheshatu zo gukuraho amasasu.Kurasa bizazana kwambara n urusaku.Ibirasa nibimwe mubipimo kugirango velue fibre nziza.
Stability Guhagarara neza
Ihinduka ryiza cyane, irwanya ubushyuhe, irwanya ruswa, irwanya ubushuhe kandi irwanya kwambara.A